不同固溶處理工藝對N08120鎳合金性能的影響

打開文本圖片集

摘要：研究了1110～1190℃固溶處理工藝對N08120鎳合金鋼板的力學性能和組織的影響。結(jié)果表明：隨著固溶處理溫度的提高，合金的塑性和表面耐蝕性變好；在1190℃下，隨著固溶時間的增加，合金的塑性和表面耐蝕性先變好再變差。

關(guān)鍵詞：N08120鎳合金；固溶熱處理；力學性能；晶間腐蝕

Effect of different solid solution heat treatment processes on the properties of N08120 nickel alloy

LIU Guohui， YIN Runbang， LI Zhanlei， ZHU Chaobing， ZHENG Zhou

Dongfang Boiler Co.， Ltd.， Deyang 618000， Sichuan， China

Abstract： Investigated the effect of solid solution heat treatment process at 1110～1190℃ on the mechanical properties and microstructure of N08120 nickel alloy steel plate. The results show that as the solution treatment temperature increases， the plasticity and surface corrosion resistance of the alloy improve; Below 1190℃，as the solid solution time increases， the plasticity and surface corrosion resistance of the alloy first improve and then deteriorate.

Keywords： N08120 nickel alloy; solid solutionheat treatment; mechanical property; intergranular corrosion