中圖分類號:U454 文獻標志碼:A 文章編號: 1000-5013(2025)04-0400-1C
NC-UHPC Interface Shear Performance Test and Simulation Based on Cohesive Zone Model
HUANG Wei1'2,WANG Ting1'2, ZHANG Yuting 1,2 ,SIBINUER·Xiamuxinu1'2,ZHOU Zhi3
(1.Hubei Key Laboratory of Theory and Application of Advanced Materials Mechanics, Wuhan University of Technology,Wuhan 430070,China;2. Department of Mechanics and Engineering Sciences,Wuhan University of Technology,Wuhan 43007o,China;3.School of Transportation and Logistics Engineering,Wuhan Universityof Technology,Wuhan 430o7o,China)
Abstract:To investigate the shear mechanism at the interface between ultra-high performance concrete (UHPC) and normal concrete (NC),nine groups of double-sided shear tests were conducted on NC-UHPC specimens,the effects of steel fiber content,concrete age,and boundary constraint conditions on interfacial mechanical properties were studied. Combining with ABAQUS software,a refined finite element model considering interfacial bond-slipcharacteristics was established,and an interfacial bond stress distribution model was constructed through theoretical derivation. The results show that under unrestrained conditions,specimens with low steel fiber content (0%-1% volume fraction) exhibit single-surface failure characteristics,while fixing the botom of theNC blocks efectively activatesa dual-surface failure mode.The steel fiber content in UHPC positively correlates with the interfacial shear strength,while the interfacial stiffness is lessaffected by the steel fiber content.The increase of UHPC age enhances interfacial stifess,while higher NC age has the inhibitory effect.The proposed finiteelement model effectively simulates the damage evolutionatthe interface, but simulates the asymmetric strain field in double-shear specimens with limitations.Based on the principle of energy conservation,the two-parameter model of interfacial load-displacement is established,and its prediction results conforms well with the test data.
Keywords:NC-UHPC interface;pushout test;digital image correlation;finite element;cohesive zone model
由于普通混凝土(NC)與超高性能混凝土(UHPC)界面強度的影響因素眾多且復雜,從上個世紀至今,國內外眾多學者進行了大量的研究,但至今仍存在可進一步深究的部分,如界面處理方式、界面粘結方式的參數影響規(guī)律、界面粘結機理等方面。(剩余10020字)
-
-
- 華僑大學學報(自然科學版)
- 2025年04期
- 鐵死亡在鼻咽癌發(fā)生發(fā)展及治療中...
- 參與肺癌靶向耐藥的IncRNA...
- 活性添加劑分散調控對 鍍銅線精...
- 近海漂浮垃圾收集器的設計與實現(xiàn)...
- 基于卷積神經網絡的石材鑲嵌工藝...
- NC-UHPC界面抗剪性能試驗...
- 溫度作用下超精電子廠房大跨度樓...
- Low-E玻璃在廈門某高校教學...
- 豫中靠崖窯民居建筑室內采光分析...
- C5-12啟動子降低rAAV1...
- 渾濁水體中模擬水生動物的識別...
- 雙空間耦合LDPC碼滑窗譯碼算...
- 基于UDP組播協(xié)議的土壤數據實...
- 采用高光譜技術的川西礦區(qū)周邊土...
- Burgers-Huxley方...
- 上半平面上 α -Bloch空...