焊接活性劑對(duì)低碳鋼焊縫成形性能的影響
打開(kāi)文本圖片集
Abstract：The penetration depth and width of the weld determine the popularity of the application of low carbon steel.Controlling the welding speed，changing the defocus amount，introducing protective gasand adjusting the welding attitude can improve the welding efect，but usually require high power laser. In this paper，the weld penetration and the grain phase morphology of the weld are improved by introducing active flux at low power. By introducing single welding aditives titanium dioxide and magnesium oxide，the weld penetration depth increased from 2 3 8 3 μ m to 2 8 2 2 μ m and 2 7 4 7 μ m ，adjusting the mass fraction of titanium dioxide and magnesium oxide in the compositeadditives，the weld penetration depth was further improved，andthe maximum penetration depth reached （204號(hào) 3 3 9 0 μ m ，which was more than 42 % higher than the weld penetration depth without welding additives.The improved welding penetration is atributed to the synergistic action of the two welding AIDS.This paper provides a general method for improving weld penetration under low power.
Keywords：low carbon steel; laser welding; low power; penetration; welding auxiliary
1序言
作為一種含碳量低的碳素結(jié)構(gòu)鋼，低碳鋼具有表面易處理、力學(xué)性能優(yōu)異和焊接性能良好等特性，其廣泛應(yīng)用于汽車(chē)、儀表殼、管道、化工設(shè)備等領(lǐng)域[1-]，其中，焊接效果決定了低碳鋼的應(yīng)用普及。（剩余4691字）