多次正火對12Cr2Ni4鋼組織性能的影響

打開文本圖片集

摘要：通過對12Cr2Ni4鋼進行兩種正火工藝試驗，對比多次正火和常規(guī)正火效果，并采用金相法檢測兩種工藝對應的金相組織。結果顯示：在正火溫度、保溫時間相同時，兩次正火處理獲得較細的珠光體組織，晶粒得到細化，鋼的強度、硬度得到提高。

關鍵詞：12Cr2Ni4鋼；多次正火；晶粒細化

Effect of multiple normalizations on the microstructure of 12Cr2Ni4 steel

WANG Quanzhen1， JIANG Mingtong2， LIU Shuangqing1， REN Fujun1， WANG Hao3

1.Shengu Group Co.， Ltd.， Shenyang 110869， Liaoning， China

2. Dalian Vocational Technical College， Dalian 116035， Liaoning， China

3. Jiamusi Electric Machine Co.， Ltd.， Jiamusi 154002， Heilongjiang， China

Abstract： Through the multiple normalizing process test of 12Cr2Ni4 steel， the effect of multiple normalizing and ordinary normalizing effect were compared and analyzed， and the metallographic structure of the two processes was detected by metallographic method. When the normalizing temperature is heated and the holding time is exactly the same， the pearlite obtained after multiple normalizing is finer， the grain is refined， and the strength and hardness of the steel are higher.

Keywords： 12Cr2Ni4 steel; multiple normalizing; grain refinement

1 序言

眾所周知，齒輪的服役工況非?？量?，因此要求齒輪用鋼應有高的硬度、耐磨性及疲勞強度。（剩余2095字）