大面積鈣鈦礦太陽(yáng)能電池薄膜制備工藝進(jìn)展綜述
打開(kāi)文本圖片集
關(guān)鍵詞：鈣鈦礦；大面積模組；太陽(yáng)能電池；制備工藝；光伏中圖分類(lèi)號(hào)：TM914.4 文獻(xiàn)標(biāo)識(shí)碼：ADOI：10.37188/CJL.20240229 CSTR：32170.14.CJL.20240229
Reviewof Advances inLarge-area Perovskite Solar Cell Thin-film Fabrication Techniques
XU Zhentong'，LIN Jie ，HUANG Jingsong2， JIANG Chengming1" （1.CollegeofMechanical Engineering，Dalian UniversityofTechnology，Dalian116ooo，China; 2.OxfordSuzhouCentreforAdvancedResearch（OSCAR），UniversityofOxford，Suzhou215123，China） *CorrespondingAuthors，E-mail：jingsong.huang@oxford-oscar.cn;jiangcm@dlut.edu.cn
Abstract：Theabundant raw materials，lowcost，high performance，and flexibilityof perovskite materials have sparked significant researchand industrial interest.Following this，perovskite solar cels（PSCs） have undergone rapid development atthelaboratory scale，thephotovoltaicconversion efficiencyhas been improved from theinitial 3.8%to 2 6 . 7 % in just a few decades.Its excellent photoelectric performance is due to the physical properties of perovskite materials，such as wide lightabsorption range，good temperaturecoeficient，adjustable band gap，high carriermobilityand strong defect tolerance.Thecommercialization of perovskite photovoltaicsdependson the successful transition from laboratory-scale perovskite solarcels to large-scale perovskite solar modules.However，as the device sizeincreases，theeficiency dropssignificantly，hindering itscommercial viability.Themainproblem lies in the preparationof high-qualityand highly uniform large-area perovskite films，which are mainly prepared by spin-coating forsmall-areadevices.However，thespin-coating method is notsuitableforlarge-areafilm preparationas itcan lead to uneven film thickness and severe waste of raw materials.Researchers have employed techniques such as blade coating，slot-diecoating，inkjet printing，andvacuumdeposition，etc.Thisarticlereviews thepreparationproesof large-area perovskite thin-filmandthecurrentresearch progressathomeand abroad，and discusses the improvementof device efficiencybyvariousaditivesand solvents，withthehopeofrealizingtheindustrializationandcommercializationof large-areaperovskite photovoltaicsas soon as possible.
Key Words：perovskite；large area module；solar cells；preparation process；solar power
1引言
鈣鈦礦太陽(yáng)能電池（PSCs）的光電轉(zhuǎn)換效率（PCE）從最初2009年的 3 . 8 % 提升至當(dāng)前的 ，這些小面積的太陽(yáng)能電池 達(dá)到了傳統(tǒng)晶硅太陽(yáng)能電池的性能水平，實(shí)現(xiàn)了顯著提升。（剩余22477字）