Study on the influence of prefabricated defect size on the internal morphology of debonding defects
XUN Guoli*， LI Yue， ZHOU Changgeng （Composite Materials Technology Center，AVIC Manufacturing Technology Institute，Beijing 100130）
Abstract：Carbon-fiber-reinforced bismaleimideresincompositelaminates withpre-fabricateddefectswere successfuly prepared.Theadhesive filmof thesameresin systemwasutilized to prepareadhesive specimenswith debonding defects throughtheadhesiveco-curing process.Ultrasonic C-scan technologywasused for non-destructive testing to confirm thelocationandsizeofdefects.Meanwhile，theinfluenceofthediameteranddepthof prefabricateddefectsontheinternal morphology of debonding defects was studied usingoptical microscopyand metalographic microscopy.Theresultsshowed thattheinternal morphologyofdefectscanbeclassified intothree types：theresin-filed typein whichtheadhesivefilm resinbasicallyfillsteinteriorofthedefectscompletely；thegas-flledtypeinwhichtheahesivefilmresinfillstheinteriorofthedefects，butthereisalargebubbleinside；andtheoutwarddifusiontypeinwhichtheadhesivefilmresinfilsthe interiorof the defects well，yet there area large number of voids distributed within it.
Keywords：adhesivedefects；internal morphology；adhesiveco-curing；adhesive joints；carbon fibercomposites
1引言
碳纖維樹脂基復(fù)合材料（CFRP）是以碳纖維為增強體、以樹脂為基體的結(jié)構(gòu)復(fù)合材料。（剩余4872字）